All couplings should undergo inner and outer surface inspection after final processing and before electroplating on the inner or outer surface. The circumferential magnetic field wet fluorescent magnetic particle method of ISO 13665 or ASTM E709 should be used to inspect surface longitudinal defects, or other non-destructive testing methods that have been proven to have the same sensitivity to the purchaser should be used for inspection. According to 10.15.4, records should be kept.
- 产品描述
-
All couplings should undergo inner and outer surface inspection after final processing and before electroplating on the inner or outer surface. The circumferential magnetic field wet fluorescent magnetic particle method of ISO 13665 or ASTM E709 should be used to inspect surface longitudinal defects, or other non-destructive testing methods that have been proven to have the same sensitivity to the purchaser should be used for inspection. According to 10.15.4, records should be kept.
9.11.2 Coupling
If specified on the order, the casing coupling should be supplied in one of the end machining forms specified in Table C-1 and Table C-2 or Table E.1 and Table E.2.
If specified on the order, the oil pipe coupling should be supplied in one of the end machining forms specified in Table C-2 or Table E.2.
000011.2 Surface inspection
9.12.1 All finished couplings should not have any defects that damage the continuity of the threads.
9.12.2 All couplings shall undergo inner and outer surface inspection after final processing and before electroplating on the inner or outer surface. The circumferential magnetic field wet fluorescent magnetic particle method of ISO 13665 or ASTM E709 should be used to inspect surface longitudinal defects, or other non-destructive testing methods that have been proven to have the same sensitivity to the purchaser should be used for inspection. According to 10.15.4, records should be kept.
9.12.3 After consultation between the purchaser and the manufacturer, non-destructive testing is not required for H40, J55, and K55 steel grade couplings. However, internal and external surface appearance inspections should be carried out after final processing and before electroplating, and there should be no visible cracks, cracks, or pores. The marking requirements are shown in Table C.48 or Table E.48.
Contact Us
Main business: American standard oil casing, pipeline pipe, Cangzhou oil casing, API oil casing, Hebei oil casing, polyurethane insulation pipe, galvanized wire steel pipe, 3PE anti-corrosion steel pipe, thickened oil pipe, large diameter oil casing, oil casing factory, insulation pipe, oil casing, anti-corrosion steel pipe, etc.
Address: Zhenggang Development Zone, Yanshan County, Hebei Province
Email:czbggy@163.com
Telephone:18831708666 18931747888